Refine
H-BRS Bibliography
- yes (38)
Departments, institutes and facilities
- Fachbereich Angewandte Naturwissenschaften (38) (remove)
Document Type
- Article (20)
- Conference Object (8)
- Report (6)
- Preprint (3)
- Part of a Book (1)
Year of publication
Keywords
- stem cells (3)
- Biomineralization (2)
- Folin-Ciocalteu assay (2)
- Miscanthus (2)
- angiogenesis (2)
- antioxidant activity (2)
- biomass (2)
- bone tissue engineering (2)
- kraft lignin (2)
- lignocellulose feedstock (2)
Polyether and polyether/ester based TPU (thermoplastic polyurethanes) were investigated with wide-angle XRD (X-ray diffraction) and SAXS (small angle X-ray scattering). Furthermore, SAXS measurements were performed in the temperature range of 30 °C to 130 °C. Polyether based polymers exhibit only one broad diffraction signal in a region of 2 θ 15° to 25°. In case of polyurethanes with ether/ester modification, the broad diffraction signal arises with small sharp diffraction signals. SAXS measurements of polymers reveal the size and shape of the crystalline zones of the polymer. Between 30 °C and 130 °C the size of the crystalline zone changes significantly. The size decreases in most of investigated TPU. In the case of Desmopan 9365D an increase of the particle size was observed.
Temperature Dependency of Morphological Structure of Thermoplastic Polyurethane using WAXS and SAXS
(2016)
Polyurethanes achieved an exceptional position among the most important organic polymers due to their highly specific technological application areas. Polyurethanes represent a polyaddition product of isocyanate and diols. In terms of their enormous industrial importance, the chemistry of isocyanates has been extensively studied.
Today, more than 70 million tons of lignin are produced by the pulp and paper industry every year. However, the utilization of lignin as a source for chemical synthesis is still limited due to the complex and heterogeneous lignin structure. The purpose of this study was a selective photodegradation of industrially available kraft lignin in order to obtain appropriate fragments and building block chemicals for further utilization, e.g. polymerization. Thus, kraft lignin obtained from soft wood black liquor by acidification was dissolved in sodium hydroxide and irradiated at a wavelength of 254 nm with and without the presence of titanium dioxide in various concentrations. Analyses of the irradiated products via SEC showed decreasing molar masses and decreasing polydispersity indices over time. At the end of the irradiation period the lignin was depolymerised to form fragments as small as the lignin monomers. TOC analyses showed minimal mineralisation due to the depolymerisation process.
Antioxidant activity is an essential feature required for oxygen-sensitive merchandise and goods, such as food and corresponding packaging as well as materials used in cosmetics and biomedicine. For example, vanillin, one of the most prominent antioxidants, is fabricated from lignin, the second most abundant natural polymer in the world. Antioxidant potential is primarily related to the termination of oxidation propagation reactions through hydrogen transfer. The application of technical lignin as a natural antioxidant has not yet been implemented in the industrial sector, mainly due to the complex heterogeneous structure and polydispersity of lignin. Thus, current research focuses on various isolation and purification strategies to improve the compatibility of lignin material with substrates and enhancing its stabilizing effect.
Antioxidant activity is an essential aspect of oxygen-sensitive merchandise and goods, such as food and corresponding packaging, cosmetics, and biomedicine. Technical lignin has not yet been applied as a natural antioxidant, mainly due to the complex heterogeneous structure and polydispersity of lignin. This report presents antioxidant capacity studies completed using the 2,2-diphenyl-1-picrylhydrazyl (DPPH) assay. The influence of purification on lignin structure and activity was investigated. The purification procedure showed that double-fold selective extraction is the most efficient (confirmed by ultraviolet-visible (UV/Vis), Fourier transform infrared (FTIR), heteronuclear single quantum coherence (HSQC) and 31P nuclear magnetic resonance spectroscopy, size exclusion chromatography, and X-ray diffraction), resulting in fractions of very narrow polydispersity (3.2⁻1.6), up to four distinct absorption bands in UV/Vis spectroscopy. Due to differential scanning calorimetry measurements, the glass transition temperature increased from 123 to 185 °C for the purest fraction. Antioxidant capacity is discussed regarding the biomass source, pulping process, and degree of purification. Lignin obtained from industrial black liquor are compared with beech wood samples: antioxidant activity (DPPH inhibition) of kraft lignin fractions were 62⁻68%, whereas beech and spruce/pine-mixed lignin showed values of 42% and 64%, respectively. Total phenol content (TPC) of the isolated kraft lignin fractions varied between 26 and 35%, whereas beech and spruce/pine lignin were 33% and 34%, respectively. Storage decreased the TPC values but increased the DPPH inhibition.
Design and characterization of geopolymer foams reinforced with Miscanthus x giganteus fibers
(2024)
This paper presents the effects of different amounts of fibers and foaming agent, as well as different fiber sizes, on the mechanical and thermal properties of fly ash-based geopolymer foams reinforced with Miscanthus x giganteus fibers. The mechanical properties of the geopolymer foams were measured through compressive strength, and their thermal properties were characterized by thermal conductivity and X-ray micro-computed tomography. Furthermore, design of experiment (DoE) were used to optimize the thermal conductivity and compressive strength of Miscanthus x giganteus reinforced geopolymer foams. In addition, the microstructure was studied using X-ray diffraction (XRD), Field emission scanning electron microscopy (SEM) and Fourier-Transform Infrared Spectroscopy (FTIR). Mixtures with a low thermal conductivity of 0.056 W (m K)−1 and a porosity of 79 vol% achieved a compressive strength of only 0.02 MPa. In comparison, mixtures with a thermal conductivity of 0.087 W (m K)−1 and a porosity of 58 vol% achieved a compressive strength of 0.45 MPa.
Approximately 45% of global greenhouse gas emissions are caused by the construction and use of buildings. Thermal insulation of buildings in the current context of climate change is a well-known strategy to improve the energy efficiency of buildings. The development of renewable insulation material can overcome the drawbacks of widely used insulation systems based on polystyrene or mineral wool. This study analyzes the sustainability and thermal conductivity of new insulation materials made of Miscanthus x giganteus fibers, foaming agents, and alkali-activated fly ash binder. Life cycle assessments (LCA) are necessary to perform benchmarking of environmental impacts of new formulations of geopolymer-based insulation materials. The global warming potential (GWP) of the product is primarily determined by the main binder component sodium silicate. Sodium silicate's CO2 emissions depend on local production, transportation, and energy consumption. The results, which have been published during recent years, vary in a wide range from 0.3 kg to 3.3 kg CO2-eq. kg-1. The overall GWP of the insulation system based on Miscanthus fibers, with properties according to current thermal insulation regulations, reaches up to 95% savings of CO2 emissions compared to conventional systems. Carbon neutrality can be achieved through formulations containing raw materials with carbon dioxide emissions and renewable materials with negative GWP, thus balancing CO2 emissions.
Polyurethane (PU) coatings were successfully produced using unmodified kraft lignin (KL) as an environmentally benign component in contents of up to 80 wt%. Lignin samples were precipitated from industrial black liquor in aqueous solution working at room temperature and different pH levels (pH 2 to pH 5). Lignins were characterized by UV-Vis, FTIR, pyrolysis-GC/MS, SEC and 31P-NMR. Results show a correlation between pH level, OH number and molecular weight Mw of isolated lignins. Lignin-based polyurethane coatings were prepared in an efficient one step synthesis dissolving lignin in THF and PEG425 in an ultrasonic bath followed by addition of 4,4-diphenylmethanediisocyanate (MDI) and triethylamine (TEA). Crosslinking was achieved under very mild conditions (1 hour at room temperature followed by 3 hours at 35 °C). The resulting coatings were characterized regarding their physical properties including ATR-IR, TGA, optical contact angle, light microscopy, REM-EDX and AFM data. Transparent homogeneous films of high flexibility resulted from lignins isolated at pH 4, possessing a temperature resistance up to 160 °C. Swelling tests revealed a resistance against water. Swelling in DMSO depends on index, pH of precipitation and catalyst utilization for PU preparation. According to AFM studies, surface roughness is between 10 and 28 nm.