Process-induced changes in the morphology of biodegradable polybutylene adipate terephthalate (PBAT) and polylactic acid (PLA) blends modified with various multifunctional chainextending cross-linkers (CECLs) are presented. The morphology of unmodified and modified films produced with blown film extrusion is examined in an extrusion direction (ED) and a transverse direction (TD). While FTIR analysis showed only small peak shifts indicating that the CECLs modify the molecular weight of the PBAT/PLA blend, SEM investigations of the fracture surfaces of blown extrusion films revealed their significant effect on the morphology formed during the processing. Due to the combined shear and elongation deformation during blown film extrusion, rather spherical PLA islands were partly transformed into long fibrils, which tended to decay to chains of elliptical islands if cooled slowly. The CECL introduction into the blend changed the thickness of the PLA fibrils, modified the interface adhesion, and altered the deformation behavior of the PBAT matrix from brittle to ductile. The results proved that CECLs react selectively with PBAT, PLA, and their interface. Furthermore, the reactions of CECLs with PBAT/PLA induced by the processing depended on the deformation directions (ED and TD), thus resulting in further non-uniformities of blown extrusion films.
This study investigates the effects of four multifunctional chain-extending cross-linkers (CECL) on the processability, mechanical performance, and structure of polybutylene adipate terephthalate (PBAT) and polylactic acid (PLA) blends produced using film blowing technology. The newly developed reference compound (M·VERA® B5029) and the CECL modified blends are characterized with respect to the initial properties and the corresponding properties after aging at 50 °C for 1 and 2 months. The tensile strength, seal strength, and melt volume rate (MVR) are markedly changed after thermal aging, whereas the storage modulus, elongation at the break, and tear resistance remain constant. The degradation of the polymer chains and crosslinking with increased and decreased MVR, respectively, is examined thoroughly with differential scanning calorimetry (DSC), with the results indicating that the CECL-modified blends do not generally endure thermo-oxidation over time. Further, DSC measurements of 25 µm and 100 µm films reveal that film blowing pronouncedly changes the structures of the compounds. These findings are also confirmed by dynamic mechanical analysis, with the conclusion that tris(2,4-di-tert-butylphenyl)phosphite barely affects the glass transition temperature, while with the other changes in CECL are seen. Cross-linking is found for aromatic polycarbodiimide and poly(4,4-dicyclohexylmethanecarbodiimide) CECL after melting of granules and films, although overall the most synergetic effect of the CECL is shown by 1,3-phenylenebisoxazoline.
Characterization methods of pressure sensitive adhesives (PSA) originate from technical bonding and do not cover relevant data for the development and quality assurance of medical applications, where PSA with flexible backing layers are adopted to human skin. In this study, a new method called RheoTack is developed to determine (mechanically and optically) an adhesion and detaching behavior of flexible and transparent PSA based patches. Transdermal therapeutic systems (TTS) consisting of silicone-based PSAs on a flexible and transparent backing layer were tested on a rotational rheometer with an 8 mm plate as a probe rod at retraction speeds of 0.01, 0.1, and 1 mm/s with respect to their adhesion and detaching behavior in terms of force-retraction displacement curves. The curves consist of a compression phase to affirm wetting; a tensile deformation phase intercepting stretching, cavity, and fibril formation; and a failure phase with detaching. Their analysis provides values for stiffness, force, and displacement of the beginning of fibril formation, force and displacement of the beginning of a failure due to fibril breakage and detaching, as well as corresponding activation energies. All these parameters exhibit the pronounced dependency on the retraction speed. The force-retraction displacement curves together with the simultaneous video recordings of the TTS deformation from three different angles (three cameras) provide deeper insight into the deformation processes and allow for interpreting the properties’ characteristics for PSA applications.
Process-dependent thermo-mechanical viscoelastic properties and the corresponding morphology of HDPE extrusion blow molded (EBM) parts were investigated. Evaluation of bulk data showed that flow direction, draw ratio, and mold temperature influence the viscoelastic behavior significantly in certain temperature ranges. Flow induced orientations due to higher draw ratio and higher mold temperature lead to higher crystallinities. To determine the local viscoelastic properties, a new microindentation system was developed by merging indentation with dynamic mechanical analysis. The local process-structure-property relationship of EBM parts showed that the cross-sectional temperature distribution is clearly reflected by local crystallinities and local complex moduli. Additionally, a model to calculate three-dimensional anisotropic coefficients of thermal expansion as a function of the process dependent crystallinity was developed based on an elementary volume unit cell with stacked layers of amorphous phase and crystalline lamellae. Good agreement of the predicted thermal expansion coefficients with measured ones was found up to a temperature of 70 °C.
This study presents a microindentation system which allows spatially resolved local as well as bulk viscoelastic material information to be obtained within one instrument. The microindentation method was merged with dynamic mechanical analysis (DMA) for a tungsten cone indenter. Three tungsten cone indenters were investigated: tungsten electrode, tungsten electrode + 2% lanthanum, and tungsten electrode + rare earth elements. Only the tungsten electrode + 2% lanthanum indenter showed the sinusoidal response, and its geometry remained unaffected by the repeated indentations. Complex moduli obtained from dynamic microindentation for high-density polyethylene, polybutylene terephthalate, polycarbonate, and thermoplastic polyurethane are in agreement with the literature. Additionally, by implementing a specially developed x-y-stage, this study showed that dynamic microindentation with a tungsten cone indenter was an adequate method to determine spatially resolved local viscoelastic surface properties.