Refine
H-BRS Bibliography
- yes (2)
Departments, institutes and facilities
- Institut für Technik, Ressourcenschonung und Energieeffizienz (TREE) (2) (remove)
Year of publication
- 2023 (2) (remove)
Language
- English (2)
A biodegradable blend of PBAT—poly(butylene adipate-co-terephthalate)—and PLA—poly(lactic acid)—for blown film extrusion was modified with four multi-functional chain extending cross-linkers (CECL). The anisotropic morphology introduced during film blowing affects the degradation processes. Given that two CECL increased the melt flow rate (MFR) of tris(2,4-di-tert-butylphenyl)phosphite (V1) and 1,3-phenylenebisoxazoline (V2) and the other two reduced it (aromatic polycarbodiimide (V3) and poly(4,4-dicyclohexylmethanecarbodiimide) (V4)), their compost (bio-)disintegration behavior was investigated. It was significantly altered with respect to the unmodified reference blend (REF). The disintegration behavior at 30 and 60 °C was investigated by determining changes in mass, Young’s moduli, tensile strengths, elongations at break and thermal properties. In order to quantify the disintegration behavior, the hole areas of blown films were evaluated after compost storage at 60 °C to calculate the kinetics of the time dependent degrees of disintegration. The kinetic model of disintegration provides two parameters: initiation time and disintegration time. They quantify the effects of the CECL on the disintegration behavior of the PBAT/PLA compound. Differential scanning calorimetry (DSC) revealed a pronounced annealing effect during storage in compost at 30 °C, as well as the occurrence of an additional step-like increase in the heat flow at 75 °C after storage at 60 °C. The disintegration consists of processes which affect amorphous and crystalline phase of PBAT in different manner that cannot be understood by a hydrolytic chain degradation only. Furthermore, gel permeation chromatography (GPC) revealed molecular degradation only at 60 °C for the REF and V1 after 7 days of compost storage. The observed losses of mass and cross-sectional area seem to be attributed more to mechanical decay than to molecular degradation for the given compost storage times.
Transdermal therapeutic systems (TTS) represent an up-to-day medication applied to human skin, which consists of a drug-containing pressure-sensitive adhesive (PSA) and a flexible backing layer. The development of a reliable TTS requires precise knowledge of the viscoelastic tack behavior of PSA in terms of adhesion and detaching. Tailoring of a PSA can be achieved by altering the resin content or modifying the chemical properties of the macromolecules. In this study, three different resin content of two silicone-based PSA – non-amine compatible, and less tack, amine-compatible – were investigated with the help of recently developed RheoTack method to characterize the retraction speed dependent tack behavior for various geometries of the testing rods. The obtained force-retraction displacement-curves clearly depict the effect of the chemical structure as well as the resin content. Decreasing the resin content shifts the start of fibril fracture to larger deformations states and significantly enhances the stretchability of the fibrils. To compare various rod geometries precisely, the force-retraction displacement curves were normalized to account for effective contact areas. The flat and spherical rods led to completely different failure and tack behaviors. Furthermore, the adhesion formation between TTS with flexible backing layers and rods during the dwell phase happens in a different manner compared to rigid plates, in particular for flat rods, where maximum compression stresses occur at the edges and not uniformly over the cross-section. Thus, the approach to follow ASTM D2949 has to be reconsidered for tests of these materials.