Polyether and polyether/ester based TPU (thermoplastic polyurethanes) were investigated with wide-angle XRD (X-ray diffraction) and SAXS (small angle X-ray scattering). Furthermore, SAXS measurements were performed in the temperature range of 30 °C to 130 °C. Polyether based polymers exhibit only one broad diffraction signal in a region of 2 θ 15° to 25°. In case of polyurethanes with ether/ester modification, the broad diffraction signal arises with small sharp diffraction signals. SAXS measurements of polymers reveal the size and shape of the crystalline zones of the polymer. Between 30 °C and 130 °C the size of the crystalline zone changes significantly. The size decreases in most of investigated TPU. In the case of Desmopan 9365D an increase of the particle size was observed.
Temperature Dependency of Morphological Structure of Thermoplastic Polyurethane using WAXS and SAXS
(2016)
Polyurethanes achieved an exceptional position among the most important organic polymers due to their highly specific technological application areas. Polyurethanes represent a polyaddition product of isocyanate and diols. In terms of their enormous industrial importance, the chemistry of isocyanates has been extensively studied.
Today, more than 70 million tons of lignin are produced by the pulp and paper industry every year. However, the utilization of lignin as a source for chemical synthesis is still limited due to the complex and heterogeneous lignin structure. The purpose of this study was a selective photodegradation of industrially available kraft lignin in order to obtain appropriate fragments and building block chemicals for further utilization, e.g. polymerization. Thus, kraft lignin obtained from soft wood black liquor by acidification was dissolved in sodium hydroxide and irradiated at a wavelength of 254 nm with and without the presence of titanium dioxide in various concentrations. Analyses of the irradiated products via SEC showed decreasing molar masses and decreasing polydispersity indices over time. At the end of the irradiation period the lignin was depolymerised to form fragments as small as the lignin monomers. TOC analyses showed minimal mineralisation due to the depolymerisation process.