This study investigates the effects of four multifunctional chain-extending cross-linkers (CECL) on the processability, mechanical performance, and structure of polybutylene adipate terephthalate (PBAT) and polylactic acid (PLA) blends produced using film blowing technology. The newly developed reference compound (M·VERA® B5029) and the CECL modified blends are characterized with respect to the initial properties and the corresponding properties after aging at 50 °C for 1 and 2 months. The tensile strength, seal strength, and melt volume rate (MVR) are markedly changed after thermal aging, whereas the storage modulus, elongation at the break, and tear resistance remain constant. The degradation of the polymer chains and crosslinking with increased and decreased MVR, respectively, is examined thoroughly with differential scanning calorimetry (DSC), with the results indicating that the CECL-modified blends do not generally endure thermo-oxidation over time. Further, DSC measurements of 25 µm and 100 µm films reveal that film blowing pronouncedly changes the structures of the compounds. These findings are also confirmed by dynamic mechanical analysis, with the conclusion that tris(2,4-di-tert-butylphenyl)phosphite barely affects the glass transition temperature, while with the other changes in CECL are seen. Cross-linking is found for aromatic polycarbodiimide and poly(4,4-dicyclohexylmethanecarbodiimide) CECL after melting of granules and films, although overall the most synergetic effect of the CECL is shown by 1,3-phenylenebisoxazoline.
Characterization methods of pressure sensitive adhesives (PSA) originate from technical bonding and do not cover relevant data for the development and quality assurance of medical applications, where PSA with flexible backing layers are adopted to human skin. In this study, a new method called RheoTack is developed to determine (mechanically and optically) an adhesion and detaching behavior of flexible and transparent PSA based patches. Transdermal therapeutic systems (TTS) consisting of silicone-based PSAs on a flexible and transparent backing layer were tested on a rotational rheometer with an 8 mm plate as a probe rod at retraction speeds of 0.01, 0.1, and 1 mm/s with respect to their adhesion and detaching behavior in terms of force-retraction displacement curves. The curves consist of a compression phase to affirm wetting; a tensile deformation phase intercepting stretching, cavity, and fibril formation; and a failure phase with detaching. Their analysis provides values for stiffness, force, and displacement of the beginning of fibril formation, force and displacement of the beginning of a failure due to fibril breakage and detaching, as well as corresponding activation energies. All these parameters exhibit the pronounced dependency on the retraction speed. The force-retraction displacement curves together with the simultaneous video recordings of the TTS deformation from three different angles (three cameras) provide deeper insight into the deformation processes and allow for interpreting the properties’ characteristics for PSA applications.
Transdermal therapeutic systems (TTS) represent an up-to-day medication applied to human skin, which consists of a drug-containing pressure-sensitive adhesive (PSA) and a flexible backing layer. The development of a reliable TTS requires precise knowledge of the viscoelastic tack behavior of PSA in terms of adhesion and detaching. Tailoring of a PSA can be achieved by altering the resin content or modifying the chemical properties of the macromolecules. In this study, three different resin content of two silicone-based PSA – non-amine compatible, and less tack, amine-compatible – were investigated with the help of recently developed RheoTack method to characterize the retraction speed dependent tack behavior for various geometries of the testing rods. The obtained force-retraction displacement-curves clearly depict the effect of the chemical structure as well as the resin content. Decreasing the resin content shifts the start of fibril fracture to larger deformations states and significantly enhances the stretchability of the fibrils. To compare various rod geometries precisely, the force-retraction displacement curves were normalized to account for effective contact areas. The flat and spherical rods led to completely different failure and tack behaviors. Furthermore, the adhesion formation between TTS with flexible backing layers and rods during the dwell phase happens in a different manner compared to rigid plates, in particular for flat rods, where maximum compression stresses occur at the edges and not uniformly over the cross-section. Thus, the approach to follow ASTM D2949 has to be reconsidered for tests of these materials.
Influence of design of extrusion blow molding (EBM) in terms of extrusion direction set-up and draw ratio as well as process conditions (mold temperature) on storage modulus of high density polyethylene EBM containers was analyzed with dynamic mechanical analysis. All three parameters - mold temperature, flow direction and draw ratio - are statistically significant and lead to relative and absolute evaluation of storage modulus. Furthermore, flow induced changes in crystallinity was analyzed by differential scanning calorimetry. Obtained data on deformation properties can be employed for more sophisticated finite element simulations with the aim to reach more sustainable extrusion blow molding production.
Process-induced changes in the morphology of biodegradable polybutylene adipate terephthalate (PBAT) and polylactic acid (PLA) blends modified with various multifunctional chainextending cross-linkers (CECLs) are presented. The morphology of unmodified and modified films produced with blown film extrusion is examined in an extrusion direction (ED) and a transverse direction (TD). While FTIR analysis showed only small peak shifts indicating that the CECLs modify the molecular weight of the PBAT/PLA blend, SEM investigations of the fracture surfaces of blown extrusion films revealed their significant effect on the morphology formed during the processing. Due to the combined shear and elongation deformation during blown film extrusion, rather spherical PLA islands were partly transformed into long fibrils, which tended to decay to chains of elliptical islands if cooled slowly. The CECL introduction into the blend changed the thickness of the PLA fibrils, modified the interface adhesion, and altered the deformation behavior of the PBAT matrix from brittle to ductile. The results proved that CECLs react selectively with PBAT, PLA, and their interface. Furthermore, the reactions of CECLs with PBAT/PLA induced by the processing depended on the deformation directions (ED and TD), thus resulting in further non-uniformities of blown extrusion films.